Taulman3D Alloy 910 is High Impact, High Durability co-polymer Alloy with a tensile strength of 8,100PSI which prints with break away support structures.
Alloy 910 is a measurable advancement in 3D Printing materials technology from taulman3D. Taulman Alloy 910 is the combined effort of chemical companies, extrusion manufactures and taulman3D to specifically develop a single material to meet as many high performance 3D Printing needs as possible. This material is easily printable and tough, with a high impact strength with lower shrinkage rates that can print as standard 245C. Additionally it is easy to break off support structures. Ideal for parts requiring high strength.
NOTE: Alloy 910 is the only Nylon based polymer that makes support removal easier than most using ABS. This filament works very well on Tier Time Up! 3D printers raft less with standard ABS settings.
Tensile Strength = 8,100PSI +
Modulus PSI = 72,932
Max Elongation at break = 31%
Print Temperature = 245C
Nozzle size = Any - (There are no particulates or additives in Alloy 910)
Print Bed =
Cold = BuildTak with coat of PVA
Hot = Glass heated to 45C with coat of PVA
(PVA is 50% water and 50% "Elmers Glue All")
Shrinkage = 0.0031 in/in
Transmission = 50%
Color = Subtle Amber - May be dyed with acid based dyes.
Recommended Nozzle Temperature 230-250 Degrees Celsius
Excellent bonding, no de-lamination
Transparent opaque white in colour
Can be died with cloths die
Heated bed 70 to 100 degrees
Will adhere to Blue 3M Painters Tape or Phenolic Build platforms (including Up! perfboard)