Introducing MINGDA S-Multi Easy Peel Support. Fast and easy to peel support materials, with customizable bonding and self-bonding strength for effortless removal. No water or solvent needed, making it eco-friendly and safe. Use with dual nozzle or two-in-one-out FDM printers.

• Smart Fiber Reinforcement Technology
MINGDA S-Multi has moderate bonding strength with the main material through formula and process adjustment, which not only ensures that the main material can be formed on the supporting surface, but also can be easily separated from the supporting surface of the main material during support removal.
• Rapid removal technology
MINGDA S-Multi greatly reduces its interlayer bonding strength through formula and process adjustment, and can be easily removed during removal.
• Safety and environmental protection
MINGDA S-Multi use process without the use of water or solvent, do not produce water pollution, safety and environmental protection.

Printing Tips

1. MINGDA S-Multi is very easy to absorb the moisture in the environment. After moisture absorption, the printing will appear wire drawing, bubble extrusion, rough printing surface and other phenomena, reducing the printing quality. It is recommended that you open the MINGDA S-Multi vacuum aluminum foil bag and immediately put the wire into the drying box (humidity controlled below 15%) for printing. Please put unused wires back into the original aluminum foil bag for sealing and storage.
2. The printing wire drawing increases, bubbles are extruded, and the printing surface quality is rough when the material is damp. Please dry the wire in an 80-100 oven for 4-6 hours to restore the printing quality of MINGDA S-Multi.
3. It is recommended to select nozzles made of hardened steel or above, which can effectively improve the printing quality. It is recommended that the thickness of the heating block should not be less than 12mm.
4. In the dual nozzle printing mode, the materials in the standby nozzle will age due to long- time heating. Before switching the printing nozzle, it is necessary to extrude the aged materials out of the nozzle. Therefore, the function of the separation wall or the wipe tower in the slicing software must be used
5. After printing, annealing treatment can be carried out on the printed copy, and then the MINGDA S-Multi step can be removed. MINGDA S-Multi can support the body material during annealing, reduce the size deformation of the body material, and improve the mechanical properties of the body material. Annealing conditions: set according to the requirements of the main material.